通过对低温高磁感取向硅钢热轧板通电加热处理,发现将热轧板以55℃/s从室温加热到1000℃后降温,在1000~950℃降温过程中保持时间2~5 s,可以获得与常化工艺等效的热轧板织构组分,根据所得结果,讨论了在热轧轧机后段增加电加热装置,从而代替常化工艺生产高磁感取向硅钢的可能性。
The hot rolled plate of low temperature high magnetic induction grain-oriented silicon steel was treated by electric heating.The experimental results showed that the hot rolled sheet with equivalent normalizing plate texture components can be obtained by heating hot rolled sheet from room temperature to 1000℃with a rate of 55℃/s and then cooled which involved maintain 2-5 s during the cooling process from 1000℃to 950℃.The possibility of adding electric heating devices in the back section of hot rolling mill was discussed according to the experimental results.
作者
王若平
毛炯辉
刘静
贾涓
刘文艳
张彦文
WANG Ruoping;MAO Jionghui;LIU Jing;JIA Juan;LIU Wenyan;ZHANG Yanwen(Central Research Institute(Qingshan),Baoshan Iron&Steel Co.,Ltd.,Wuhan 430080,China;School of Materials and Metallurgy,Wuhan University of Science and Technology.Wuhan 430081,China)
出处
《电工钢》
2021年第4期1-6,共6页
ELECTRICAL STEEL
关键词
低温高磁感取向硅钢
热轧板
通电加热
常化
织构
low temperature high magnetic induction grain-oriented silicon steel
hot rolled plate
electrical heating
normalizing
texture components