摘要
为制备具有高光热转换效率的纺织材料,采用水热合成法制备了近红外吸收能力强的三维二硫化钼(MoS2)纳米颗粒,然后添加至聚氨酯(PU)纺丝液中,通过静电纺丝方法制备MoS2/PU复合光热纤维膜。借助扫描电子显微镜、透射电子显微镜、X射线粉末衍射仪、傅里叶变换红外光谱仪等对MoS2纳米颗粒及MoS2/PU复合纤维膜的结构和性能进行表征。结果表明:经功率密度为0.8 W/cm2的近红外光照射1 min后,MoS2/PU复合纤维膜的温度上升10.48℃,光热效率达到了31.07%,且经长时间反复升降温后热效应无衰减现象,同时在阳光下照射5 min后,复合纤维膜温度上升比黑色纯PU纤维膜高31%;经高温以及模拟汗液浸渍24 h后,复合纤维膜仍可保持原有强力;该MoS2/PU复合纤维膜可将光能有效地转换成热能,并具有较好的力学稳定性。
To prepare textile materials with high photothermal conversion efficiency,three-dimensional MoS2 nanoparticles with strong near-infrared absorption capacity were prepared by hydrothermal synthesis.MoS2 nanoparticles were added to polyurethane(PU)spinning solution,and MoS2/PU composite photothermal fibrous membranes was prepared by electrospinning.The structure and properties of MoS2 nanoparticles and MoS2/PU composite fibrous membranes were characterized by scanning electron microscopy,transmission electron microscopy,X-ray diffractometer powder diffraction and fourier transform infrared spectrometer.The results show that after 0.8 W/cm2 near-infrared light irradiation for 1 min,the temperature of MoS2/PU composite fibrous membranes rises by 10.48℃,and the photothermal conversion efficiency was increased up to 31.07%.After a long time of repeated temperature rises and falls,the thermal effect did not decay.At the same time,the temperature rose 31%higher than the black PU fibrous membranes under the sunlight irradiation for 5 min.After high temperature treatment and immersion in simulated sweat for 24 hours,the composite fiber membrane still maintain its original strength.In summary,the MoS2/PU composite fibrous membranes have excellent photothermal properties.It can effectively convert light energy into heat energy,and maintain excellent structural stability.
作者
曹元鸣
郑蜜
李一飞
翟旺宜
李丽艳
常朱宁子
郑敏
CAO Yuanming;ZHENG Mi;LI Yifei;ZHAI Wangyi;LI Liyan;CHANG Zhuningzi;ZHENG Min(College of Textile and Clothing Engineering, Soochow University, Suzhou, Jiangsu 215123, China)
出处
《纺织学报》
EI
CAS
CSCD
北大核心
2021年第9期46-51,58,共7页
Journal of Textile Research
基金
国家创新人才博士后计划项目(BX20190228)
江苏省产学研前瞻项目(L211500410)。
关键词
功能材料
光热转换
近红外光照射
静电纺丝
二硫化钼/聚氨酯复合纤维膜
functional material
photothermal conversion
near-infrared radiation
electrospinning
MoS2/polyurethane composite fibrous membrane