摘要
A new radiation-hard germano-silicate glass optical fiber with a pure silica glass buffer and a boron-doped silica glass inner cladding was fabricated for temperature sensor application based on the fiber Bragg grating(FBG)underg-ray irradiation environment.The temperature dependences of optical attenuation at 1550.5 nm and Bragg reflection wavelength shift from 18℃to 40℃before theγ-ray irradiation were about 4.57´10^(-4)dB/℃and 5.48 pm/℃,respectively.The radiation-induced optical attenuation at 1550.5 nm and the radiation-induced Bragg reflection wavelength shift under theγ-ray irradiation with the total dose of 22.85 kGy at 35℃were about 0.03 dB/m and 0.12 nm,respectively,with theγ-ray irradiation sensitivity of 5.25´10^(-3)pm/Gy.The temperature and theγ-ray irradiation dependence of optical attenuation at 1550.5 nm in the FBG written fiber with boron-doped silica glass inner cladding were about 6 times and 4 times lower than that in the FBG written fiber without boron-doped silica glass inner cladding under a temperature change from 18℃to 40℃and theγ-ray irradiation with the total dose of 22.85 kGy at 35℃,respectively.Furthermore,the effect of temperature increase on the Bragg reflection wavelength of the FBG written fiber with boron-doped silica inner cladding was much larger about 1000 times than that of theγ-ray irradiation.However,no influence on the reflection power of the Bragg wavelengths and the full width at half maximum(FWHM)bandwidth under temperature and theγ-ray irradiation change was found.Also,after theγ-ray irradiation with the dose of 22.85 kGy,no significant change in the refractive index was found but the residual stresses developed in the fiber were slightly relaxed or retained.
基金
This work was partially supported by the Korea Electric Power Corporation Research Institute(Grant No.KEPRI-16-23)
the Korea Industrial Complex Corporation Industrial Cluster Competitiveness Enhancement Project(Grant No.RGJ18014),South Korea.