Ultra-small PbSe quantum dots (QDs) were synthesized using conventional hot-injection method.A small amount of Sn was used as a nucleation promotion agent to control nucleation and growth during the QDs synthesis process.The average diameter of the QDs is about 1.6 nm,of which absorption peak centers at 550 nm and photoluminescence peak centers at 750 nm under 350 nm laser excitation with power as low as 500 μW.Transmission electron microscopy images confirm that the QDs size well matches with the calculated diameter from Brus equation.This match and electron energy loss spectroscopy analysis proves that Sn is not involved into the final structure of the ultra-small PbSe QDs.An ion-exchange process was proposed for the nucleation control and ultra-small QDs synthesis.The prepared ultra-small QDs could be a promising candidate for luminescence,solar cell devices,and others.
作者
程方亮
YU Miao
JIA Linyuan
TIAN Qihang
张继红
Bokhyeon Kim
ZHAO Xiujian
CHENG Fangliang;YU Miao;JIA Linyuan;TIAN Qihang;ZHANG Jihong;Bokhyeon Kim;ZHAO Xiujian(State Key Laboratory of Silicate Materials for Architectures,Wuhan University of Technology,Wuhan 430070,China;Advanced Photonics Research Institute,Gwangju Institute of Science and Technology,Oryongdong,Buk-gu,Gwangju 500-712,Korea)
基金
Funded by the Opening Funding of the State Key Laboratory of Silicate Materials for Architecture (SYSJJ2018-06)
the Fundamental Research Funds for the Central Universities Wuhan University of Technology,China (WUT:2016IVA096)
the Research Program (No. S2634339) through a Grant Provided by the Ministry of SMEs and Startups
the Research on Advanced Optical Science and Technology through a Grant Funded by the GIST,Korea。