利用搅拌摩擦连接技术对2024/6061异质铝合金进行连接,分析不同的搅拌头旋转速度和搅拌头前进速度比值变化对连接区性能的影响规律。结果显示当搅拌头旋转速度一定的情况下,随着搅拌头旋转速度与前进速度比值的降低其连接区域的金相组织融合度降低,且靠近2024铝合金交界区域金属塑化变形严重,而靠近6061铝合金边交界区域金属塑性变形程度低;各试样的连接区域硬度均比2024铝合金硬度低,但比6061铝合金硬度高;各试样的抗拉强度均比两母材低,但断裂形状一样,呈45°角剪切状。
In this paper,friction stir joint technology is used to joint 2024/6061 heterogeneous aluminum alloy,and the influence of different tool rotation speed and tool forward speed ratio on the performance of the joint is analyzed.The results show that when the rotating speed of the tool is constant,the degree of microstructure fusion decreases with the decrease of the ratio of the rotating speed to the forward speed,and the plastic deformation of the metal near the interface area of 2024 aluminum alloy is noticeable.But the plastic deformation of the metal near the interface area of 6061 aluminum alloy is low.The hardness of the jointing region of each sample is lower than 2024 aluminum alloy,but higher than 6061 aluminum alloy;The tensile strength of each sample is lower than that of the two base metals,and the fracture shape is the same,which is shear at an angle of 45°.
作者
王谋之
朱增宝
姜迪
宋娓娓
Wang Mouzhi;Zhu Zengbao;Jiang Di;Song Weiwei(School of Mechanical Engineering,Anhui University of Science&Technology,Huainan 232001,China;College of Mechanical and Electrical Engineering,Huangshan University,Huangshan 245041,China)
出处
《黄山学院学报》
2021年第5期37-40,共4页
Journal of Huangshan University
基金
安徽省重点研发与开发计划项目(202004a05020025
202104b11020011)
中国博士后基金项目(2016M600411)
安徽省仿真设计与现代制造工程技术研究中心开放课题(SGCZXZD1801
SGCZXZD1901)
安徽省青年优秀人才支持项目(gxyq2019086)。
关键词
搅拌摩擦连接
异种铝合金
硬度
抗拉强度
金相组织
friction stir joint
heterogeneous alloy
hardness
tensile strength
microstructure