制备了SFM-GDC‖GDC‖BCFN结构的陶瓷阳极支撑单电池,H_(2)气氛中700℃下最大功率密度可达188 mW/cm^(2).稳定运行50 h无明显衰减,显示该电池具有很好的工作稳定性.SFM-GDC陶瓷阳极表现出很好的耐积碳性能,阳极通入CH_(4),700℃最大功率密度为70 mW/cm^(2),运行40 h,性能无明显衰减,电压保持在0.56 V.
The structure of SFM-GDC‖GDC‖BCFN single cell supported by ceramic anode was fabricated,the maximum power density reached to 188 mW/cm^(2) in H_(2)under 700℃.The electrochemical activity and stability of the cell also perform well in 50 h.SFM-GDC ceramic anode also shows good coking-resistance in CH_(4) atmosphere,in this case the maximum power density was 70 mW/cm^(2) at 700℃.After 40 h operation,the performance of the cell has no obvious attenuation and the voltage is kept at 0.56 V.
作者
徐娜
祝梦宇
滕茹煊
苏少辉
张继元
徐占林
XU Na;ZHU Meng-yu;TENG Ru-xuan;SU Shao-hui;ZHANG Ji-yuan;XU Zhan-lin(Key Laboratory of Preparation and Application of Environmental Friendly Materials,Ministry of Education,Jilin Normal University,Changchun 130103,China;College of Chemistry,Jilin Normal University,Siping 136000,China)
出处
《吉林师范大学学报（自然科学版）》
2021年第4期15-18,共4页
Journal of Jilin Normal University:Natural Science Edition
基金
吉林省发展和改革委员会产业技术研究与开发项目(2020C026-4)
吉林省教育厅科学技术项目(JJKH20200423KJ)。