3D Ultralight Hollow NiCo Compound@MXene Composites for Tunable and High-E cient Microwave Absorption

The 3D hollow hierarchi-cal architectures tend to be designed for inhibiting stack of MXene flakes to obtain satisfactory lightweight,high-e cient and broadband absorbers.Herein,the hollow NiCo compound@MXene networks were prepared by etching the ZIF 67 template and subsequently anchoring the Ti_(3)C_(2)Tx nanosheets through electrostatic self-assembly.The electromagnetic parameters and microwave absorption property can be distinctly or slightly regulated by adjusting the filler loading and decoration of Ti_(3)C_(2)Tx nanoflakes.Based on the synergistic e ectsof multi-components and special well-constructed structure,NiCo layered double hydroxides@Ti_(3)C_(2)Tx(LDHT-9)absorber remarkably achieves unexpected e ective absorption bandwidth(EAB)of 6.72 GHz with a thickness of 2.10 mm,covering the entire Ku-band.After calcination,transition metal oxide@Ti_(3)C_(2)Tx(TMOT-21)absorber near the percolation threshold possesses minimum reflection loss(RLmin)value of-67.22 dB at 1.70 mm within a filler loading of only 5 wt%.This work enlightens a simple strategy for constructing MXene-based composites to achieve high-e cient microwave absorbents with lightweight and tunable EAB.