In order to well arrange active sites and avoid byproducts, the reasonable structured carrier nanocatalyst plays a crucial role in high catalytic performance, but still remains a challenge. Herein, the layered CuNi-Cu_(2)O/NiAlO_(x) nanosheets have been constructed through hydrothermal synthesis followed by calcination and H_(2) reduction treatment process. The in-situ formed CuNi nanoalloys (NAs) and nano-Cu_(2)O were evenly distributed on the bilateral surface of layered NiAlOx nanosheets. Based on the planar structure of nanosheet, the synergy between catalytic active CuNi NAs and photocatalytic active nano-Cu_(2)O endows CuNi-Cu_(2)O/NiAlO_(x) nanosheets with rapid conversion efficiency for catalyzing p-nitrophenol (p-NP, 14 mg·L^(−1)) to p-aminophenol (p-AP) in 32 s with the reaction rate constant k up to 0.1779 s−1, and no obvious performance decay can be observed even over 27 cycles. Moreover, high concentration of p-NP at 10 and 20 g·L^(−1) could be reduced to p-AP within 14 and 20 min, respectively. Such designed nanoalloy/bimetal-oxide heterostructure can provide a solution for rapid conversion of aminoaromatics from nitroaromatics wastewater even at a large concentration range.
基金
This work was supported by the National Natural Science Foundation of China(Nos.21771140,51979194,and 51771138)
We really appreciate the support by the state key laboratory of fine chemicals,Dalian University of Technology(No.KF 2001).