摘要
The effect of pH value and different kinds of anions on the corrosion behavior of Cu/Al casting-rolled clad plates in the alkaline solution was evaluated by means of scanning electron microscopy(SEM),energy dispersive spectroscopy(EDS),X-ray diffraction(XRD),weight loss analysis,3D confocal laser scanning microscopy(CLSM)and electrochemical test.Results show the corrosion mainly occurs on the aluminum side.The corrosion resistance of the Cu/Al decreases as the pH value increases.When pH≥12,the dissolution of the film layer is faster than the passivation process.The addition of Cl^(-)ions reduces the corrosion resistance of the Cu/Al clad plates,which leads to pitting corrosion.The higher the concentration of Cl^(-)ions,the more prone the pitting to occur.The addition of SO_(4)^(2-)ions causes the denudation of the samples.The corrosion resistance of the Cu/Al is better in the alkaline solution containing NO_(3)^(-)ions than that in the solution containing Cl^(-)ions or SO_(4)^(2-)ions.When adding SO_(4)^(2-),NO^(3)^(-)and Cl^(-)to the pure alkaline solution,the corrosion resistance of the Cu/Al clad plates decreases.
基金
financially supported by the National Natural Science Foundation of China(No.52001216)。