Homogeneous Zr and Ti co-doped SBA-15 with high specific surface area:preparation,characterization and application

A facile synthesis procedure is proposed to prepare homogeneous Zr and Ti co-doped SBA-15(Zr-Ti-SBA-15)with high specific surface area of 876.0m2 g−1.Based on“masking mechanism”from tanning,lactic acid was used as masking agent to obtain the uniform distribution of Zr and Ti species in the SBA-15 framework.The obtained materials were characterized by powder X-ray diffraction(XRD),nitrogen adsorption-desorption isotherms,scanning electron microscope(SEM),transmission electron microscope(TEM)and X-ray photoelectron(XPS).The results reveal that in mesoporous materials,the presence of lactic acid gives rise to the uniform distribution of Zr and Ti species.The adsorption equilibrium and kinetic studies of Zr-Ti-SBA-15 materials show that the adsorption process conforms to the Langmuir isotherm and pseudo-second-order kinetic model,respectively.Regenerational experiments show that the Zr-Ti-SBA-15 displays a significant adsorption ability for methylene blue(MB)(up to 291.6 mg/g),along with good reusability,indicating promising potentials of commercialization.Methodologically,this work provides a wide range of possibilities for further development of SBA-15 based on bimetallic and sewage disposal.