This study investigates the bulk density,sintering behaviour,and microwave dielectric properties of the MgO-2B_(2)O_(3) series ceramics synthesised by solid-state reaction.According to the X-ray diffraction and microstructural analyses,the as-prepared MgO-2B_(2)O_(3) ceramics possess a single-phase structure with a rod-like morphology.The effects of different quantities of H_(3)BO_(3) and BaCu(B_(2)O5)(BCB)on the bulk density,sintering behaviour,and microwave dielectric properties of the MgO-2B_(2)O_(3) ceramics were investigated.Accordingly,the optimal sintering temperature was obtained by adding 30 wt%H_(3)BO_(3) and 8 wt%BCB.We also reduced the sintering temperature to 825°C.Furthermore,the addition of 40 wt%H_(3)BO_(3) and 4 wt%BCB increased the quality factor,permittivity,and temperature coefficient of resonance frequency of MgO-2B_(2)O_(3) to 44,306 GHz(at 15 GHz),5.1,and-32 ppm/℃,respectively.These properties make MgO-2B_(2)O_(3) a viable low-temperature co-fired ceramic with broad applications in microwave dielectrics.
基金
supported by the National Natural Science Foundation of China(Nos.61761015 and 12064007)
the Natural Science Foundation of Guangxi(Nos.2018GXNSFFA050001,2017GXNSFDA198027,and 2017GXNSFFA198011)
High Level Innovation Team and Outstanding Scholar Program of Guangxi Institutes.