摘要
In this paper,the microstructure of narrow gap laser welded joint of 45 mm Ti6321 titanium alloy was characterized.The microstructure characteristics of Laser self-fusion and laser-multi-pass-narrow-gapfilling layer were observed by metallographic microscope,and the phase morphology was analyzed by transmission electron microscope.The results show that the joint was obtained using the laser-multipass-narrow-gap welding,and no volumetric defect is observed.The weld grain of self fusion welded bead tends to be equiaxed with lots of needleα’,and the width of weld metal needleα’was 0.4μm.The heat affected zone is columnar crystal with lamellarα,and The width of heat affected zonelamellarαwas 2–4μm with a large number of dislocation tangles.The weld grains of laser-multi-pass-narrow-gap filler bead are coarse columnar grains with staggered acicularα’,and the width of acicularα’in weld metal is less than 1μm with number of dislocations.The heat affected zone is thick lamellar microstructure with a width of 2–4μm with a large number of dislocation entanglement and packing.The microstructure evolution law is related with heating temperature and cooling rate.
基金
supported by the Luoyang Ship Material Institute's Scientific and Technological Innovation Project(LW190801)
Zhengzhou Luoyang and Xinxiang Independent Innovation Demonstration Area(Porject No.201200211400).