As a potent nucleating substrate forα-Mg grain,MgAl_(2)O_(4) powder was used to inoculate the Mg-Al melt in this study.The effects of MgAl_(2)O_(4)amount,holding time and Al content on the grain size and grain refining ratio of the inoculated Mg-Al alloys are systematically investigated.The results show that the minimum grain size of Mg-3Al alloy is achieved by adding 2wt.%MgAl_(2)O_(4)powder and this alloy exhibits higher grain refining ratio than Mg-5Al and Mg-8Al alloys.The crystallographic misfit calculation indicates the wellmatching and possible orientation relationships(ORs)betweenα-Mg and MgAl_(2)O_(4).Among these predicted ORs,[10–10]α−Mg//[110]MgAl2O4 in(0002)α−Mg//(1–13)MgAl2O4 possesses the smallest misfit,i.e.,2.34%(fr).Both results of the experiment and crystallographic calculation demonstrate that the grain refinement of Mg-Al alloys is attributed to the MgAl_(2)O_(4)particles acting as the heterogeneous nucleation substrates forα-Mg grains.