摘要
采用热注入法制备Ce^(3+)掺杂CsPbBr_(3)纳米晶,利用XRD、TEM、XPS、UV-Vis、PL、Time-resolved fluorescence spectroscopy、J-V曲线测试等对样品的晶体结构、微观形貌、化学组成、光吸收性能、发光性能、荧光寿命和荧光太阳能集光器(LSC)的光学效率进行表征。实验结果表明:采用热注入法成功制备出分散性良好、平均晶粒大小为12.26 nm的立方相Ce^(3+)掺杂CsPbBr_(3)纳米晶。Ce^(3+)掺杂CsPbBr_(3)纳米晶的光学带隙和荧光发射峰强度随着Ce/Pb摩尔比的增加呈现先增大后减小的变化趋势,当n(Ce)/n(Pb)=0.25时,光学带隙达到最大为2.416 eV,发光强度最强,荧光发射峰由纯CsPbBr_(3)纳米晶的515 nm蓝移到510 nm,Ce^(3+)掺杂CsPbBr_(3)纳米晶的发光性能与稳定性均得到增强。Ce^(3+)掺杂CsPbBr_(3)纳米晶与聚苯乙烯溶液制备复合薄膜型LSC器件的光学效率η_(opt)最高达到6.81%。
The Ce^(3+)doped CsPbBr_(3) nanocrystals were prepared by hot-injection method,the crystal phase structure,micro-morphology,chemical composition,light absorption performance,luminescence performance,fluorescence lifetime and optical efficiency of luminescent solar concentrators(LSC)devices were characterized by XRD,TEM,XPS,UV-Vis,PL,Time-resolved fluorescence spectroscopy and J-V curve test.The experimental results show that the cubic phase Ce^(3+)-doped CsPbBr_(3) nanocrystals with good dispersion and average grain size of 12.26 nm are successfully prepared by hot-injection method.The optical band gap and fluorescence emission peak intensity of Ce^(3+)doped CsPbBr_(3) nanocrystals shows a trend of increasing and then decreasing with the increase of Ce/Pb molar ratio.When n(Ce)/n(Pb)=0.25,the optical band gap reaches a maximum of 2.416 eV,the luminescence intensity is the strongest,and the fluorescence emission peak blue-shifts from 515 nm to 510 nm for pure CsPbBr_(3) nanocrystals.The luminescence performance and stability of Ce^(3+)doped CsPbBr_(3) nanocrystals are enhanced.The optical efficiency η_(opt) of Ce^(3+)doped CsPbBr_(3) nanocrystals with polystyrene solution for the preparation of composite thin-film LSC is up to 6.81%.
作者
夏冬林
付陈承
XIA Donglin;FU Chencheng(State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, China;School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China)
出处
《人工晶体学报》
CAS
北大核心
2021年第12期2246-2254,共9页
Journal of Synthetic Crystals
基金
国家自然科学基金(51772230)。