微波辅助解离钒钛磁铁矿有限元分析及试验研究

FEM analysis and experimental study of microwave assisted separation of vanadium-titanomagnetite

以攀西钒钛磁铁矿为研究对象,通过有限元模拟,从理论上进行了微波对其选择性解离的可行性分析,开展了微波功率和处理时间对其解离的影响试验。采用扫描电子显微镜(SEM)、X射线衍射(XRD)、BET比表面积检测、粒度分析等方法探究了微波处理对钒钛磁铁矿解离特性的影响规律。结果表明,在微波功率3 kW,处理时间40 s的条件下,矿石可快速升温至600℃;经微波处理后,矿石内部出现许多明显裂纹,矿石比表面积和孔隙体积分别提高46.04%和83.45%;磨矿产品中-0.160 mm和-0.074 mm粒级的产率可分别提高21.47%和16.68%,邦德磨矿功指数下降8.13%。磁选试验表明,微波处理可使精矿铁品位提高2.34%,铁回收率提高1.13%。由此说明微波处理有助于钒钛磁铁矿的选择性解离,提高选别效果。

Taking vanadium-titanomagnetite(VTM)from Panxi zone as the investigation object,the feasibility of microwave selective separation of VTM was analyzed theoretically through finite element simulation,and the effects of microwave power and treatment time on its dissociation were investigated.The influence of microwave treatment on the separation characteristics of VTM were studied by using scanning electron microscope(SEM),X-ray diffraction(XRD),BET specific surface area detection method(BET),particle size analysis and other methods.The results showed that the ore can be rapidly heated up to 600℃under the condition of microwave power of 3 kW and treatment time of 40 s.After microwave treatment,many obvious cracks appeared in the ore,and the specific surface area and pore volume of VTM increased by 46.04%and 83.45%,respectively.The fractions of product with size of-0.160 mm and-0.074 mm in the grinding products increased by 21.47%and 16.68%,respectively,while the Bond grinding work index decreased by 8.13%.The magnetite separation test shows that the iron grade and recovery of concentrate can be increased by 2.34%and 1.13%respectively after microwave treatment.It is demonstrated that microwave treatment is positive to the selective separation of VTM and improve the separation effect.