Submerged arc welding(SAW) and gas metal arc welding(GMAW) experiments of Nb-bearing X80 steel were conducted with high-toughness wires.The inclusions in weld metals were analyzed in terms of their types and sizes.In GMAW,the inclusions are primarily Ti, Ca, Si, Al, and Mg compounds with no Nb and are generally less than 0.8 μm in size, whereas, in SAW weld, the inclusions are larger, mostly approximately 2-5 μm in size, and are cored with Ca and Ti, exhibiting obvious oxidation metallurgical features.The SAW joint was hot-deformed, and Nb-bearing nano precipitates were newly found in the weld metal through transmission electron microscopy, and Nb-free core-shell inclusion was found through scanning electron microscopy.The inclusions and precipitates were dispersed in or on the boundaries of acicular ferrite, contributing to acicular ferrite nucleation and grain refinement.