品质工程背景下钢筋混凝土工程耐久性关键指标

Quality Engineering Under the Background of the Durability of Reinforced Concrete Engineering Key Indicators
下载PDF
导出
摘要 钢筋混凝土耐久性能对工程建设质量具有非常重要的影响,而在品质工程创建背景下,工程建设质量的优质耐久显得更加突出。通过对规范、技术文件的梳理,在问卷调研分析的基础上,结合江苏省公路水运工程质量检测实际情况,开展了钢筋混凝土工程关键指标的分析与研究,得出以下结论:(1)应重点加强对实体指标的控制,做到事前防范,事中控制,事后改善;(2)提出的关键指标可作为日常监督检测的主要内容,有助于提升工程耐久性。 Reinforced concrete durability performance has a very important influence on the construction quality,and under the background of creating quality engineering,engineering construction quality of high quality durable appears more prominent.This article through to the specifications,technical documents,on the basis of the questionnaire survey analysis,combining with the actual situation of our province highway engineering quality,carry out the key indicators of analysis and research of reinforced concrete engineering,the following conclusions:1,should focus on strengthening the control of the entity index,do advance prevention,matter controls,afterwards improvement;2,put forward the key indicators can be used as the main content of the daily supervision and detection,help to improve the durability of engineering.
作者 王正 俞先江 孙振锋 顾冕 WANG Zheng;YU Xian-jiang;SUN Zhen-feng;GU Mian(China Design Institute Co.,Ltd,Nanjing,Jiangsu,210014,China)
出处 《黑龙江交通科技》 2021年第12期145-147,共3页 Communications Science and Technology Heilongjiang
关键词 品质工程 钢筋混凝土 耐久性 关键指标 quality engineering reinforced concrete durability key indicators
  • 相关文献

参考文献2

二级参考文献14

  • 1Wang X H, Liu X L. Modelling Effects of Corrosion on Cover Cracking and Bond in Reinforced Concrete [ J ]. Magazine of Concrete Research, 2004, 56(4) : 191-199.
  • 2Liu Y, Weyers R E. Modeling the Time-to-corrosion Cracking in Chloride Contaminated Reinforced Concrete Structures[J ]. ACI Material Journal, 1998 , 98 (6) : 675 -681.
  • 3Dagher. Finite Element Modeling of Corrosion Damage in Concrete Structure[ J ]. ACI Structural Journal, 1992 ( 6 ) : 699-708.
  • 4Liu Youping. Modeling the Time-to-corrosion Cracking of the Cover Concrete in Chloride Contaminated Reinforced Concrete Structures[D]. Virginia: Virginia Polytechnic Institute and State University, 1996.
  • 5Pantazopoulou S J, Papoulia K D. Modeling Cover-cracking due to Reinforcement Corrosion in RC Structures[J]. Journal of Engineering Mechanics, 2001, 127(4) :342-351.
  • 6Tepfers R. Cracking of Concrete Cover Along Anchored Deformed Reinforcing Bars [J ]. Magazine of Concrete Research, 1979, 31(3) :3-12.
  • 7Al-Sulaimani G J ,Kaleemullah M,Basunbul I A,et al. Influence of Corrosion and Cracking on Bond Behavior and Strength of Reinforced Concrete Members[J ]. ACI Structural Journal, 1990, 87(2) : 220-231.
  • 8Andrade C, Alonso C, Molina F J. Cover Cracking as a Function of Bar Corrosion:Part Ⅰ- Experimental Test[J]. Materials and Structures, 1993, 26(8) :453-464.
  • 9金伟良,赵羽习,鄢飞.钢筋混凝土构件的均匀钢筋锈胀力的机理研究[J].水利学报,2001,32(7):57-62. 被引量:86
  • 10张伟平,张誉.混凝土中钢筋锈胀过程的计算机仿真分析[J].同济大学学报(自然科学版),2001,29(11):1374-1377. 被引量:25

共引文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部