Improving Na^(+)transport kinetics and Na^(+)storage of hierarchical rhenium-nickel sulfide(ReS_(2)@NiS_(2))hollow architecture by assembling layered 2D-3D heterostructures

Mixed metal sulfides have been widely used as anode material of sodium-ion batteries(SIBs)because of their excellent conductivity and sodium ion storage performance.Herein,ReS_(2)@NiS_(2)heterostructures have been triumphantly designed and prepared through anchoring ReS_(2)nanosheet arrays on the surface of NiS_(2)hollow nanosphere.Specifically,the carbon nanospheres was used as hard template to synthesize NiS_(2)hollow spheres as the substrate and then the ultrathin two-dimensional ReS_(2)nanosheet arrays were uniformly grown on the surface of NiS_(2).The internal hollow property provides sufficient space to relieve the volume expansion,and the outer two-dimensional nanosheet realizes the rapid electron transport and insertion/extraction of Na^(+).Owing to the great improvement of the transport kinetics of Na^(+),NiS_(2)@ReS_(2)heterostructure electrode can achieve a high specific capacity of 400 mAh/g at the high current density of 1 A/g and still maintain a stable cycle stability even after 220 cycles.This hard template method not only paves a new way for the design and construct binary metal sulfide heterostructure electrode materials with outstanding electrochemical performance for Na^(+)batteries but also open up the potential applications of anode materials of SIBs.