A guide to use fluorinated aromatic bulky cations for stable and high-performance 2D/3D perovskite solar cells:The more fluorination the better?

While serious stability issues impede the commercialization of perovskite solar cells(PSCs),two-dime nsional(2D)perovskites based on fluorinated bulky cations have emerged as more intrinsically stable materials.However,the influence of fluorination degree of the bulky aromatic cation on the per-formance of resulting PSCs has not been scrutinized.Here,2D perovskites(FxPEA)_(2)PbI_(4)(x=1,2,3,5)are grown in situ on the surface of the three-dime nsion al(3D)perovskite and dem on strate effective passivation of the surface defects of 3D perovskite.The power conversion efficiency(PCE)of the optimized devices were boosted from 20.75%for the control device to 21.09%,22.06%,22.74%and 21.86%for 2D/3D devices treated with 4-fluorophenethylamine iodide,3,5-difluorophenylethylamine iodide,2,4,5-trifluoroethylphenylethylamine iodide,and 1,2,3,4,5-pentafluorophenylethylamine iodide,respectively.We firstly reported two unexplored RP-type layered perovskites with F_(2)PEAI and F_(3)PEAI as bulky cations.The combined experimental and theoretical analysis revealed the reasons behind the various morphology,device performances,dynamic behavior,and humidity stability.The best performing F_(5)PEAI-treated device retaining 95.0%of its initial PCE under ambient atmosphere(with RH of 60%±5%)without encapsulation for 300 h storage.This work provides useful guidance for selecting fluorinated bulky cations with different molecular electronic properties,which will play an essential role in further improving the performance/stability of PSCs for the sake of further commercialization.