研究了水稻秸秆体积掺量对硫氧镁泡沫轻质保温材料性能的影响,测试了掺水稻秸秆硫氧镁泡沫轻质保温材料的干缩量、吸水率、导热系数、抗压强度、抗折强度,并进行了微观孔结构试验。结果表明:随着水稻秸秆体积掺量的增加,硫氧镁泡沫轻质保温材料的干缩量、吸水率、导热系数和抗压强度均逐渐降低,抗折强度在一定范围内有所增加;水稻秸秆的理想体积掺量为15%~45%。
The effect of rice straw volume content on the performance of magnesium oxysulfide foam lightweight insulation materials was studied.The dry shrinkage,water absorption,thermal conductivity,compressive strength and flexural strength of the magnesium oxysulfide foam lightweight insulation materials mixed with rice straw were tested,and the microscopic pore structure test was carried out.The results show that with the increase of rice straw volume content,the dry shrinkage,water absorption,thermal conductivity and compressive strength of the magnesium oxysulfide foam lightweight insulation materials gradually decrease,but the flexural strength increases within a certain range.The reasonable volume content of rice straw is 15%~45%.
作者
姜俊玮
张鑫
刘巧玲
类成邦
任建国
JIANG Jun-wei;ZHANG Xin;LIU Qiao-ling;LEI Cheng-bang;REN Jian-guo(School of Civil Engineering,Shandong Construction University,Jinan 250101,China;Key Laboratory of Building Structural Retrofitting and Underground Space Engineering of Ministry of Education,Shandong Construction University,Jinan 250101,China)
出处
《混凝土与水泥制品》
2022年第3期91-95,共5页
China Concrete and Cement Products
基金
国家自然科学基金项目(52078282)
国家自然科学基金重点项目(52038006)。
关键词
水稻秸秆
轻质保温材料
硫氧镁水泥
力学性能
导热系数
微观试验
Rice straw
Lightweight insulation material
Magnesium oxysulfide cement
Mechanical property
Thermal conductivity
Microscopic test