摘要
准噶尔南缘区块是新疆油田增储上产的重点区块,井深6000~8000 m,预测井底温度为160℃,井底压力为170 MPa,属于典型的"三超"井。在该井区耐高温高压超高密度水泥浆基本性能的基础上,针对高温高压下超高密度水泥石的力学性能进行了研究。重点结合井下实际强度发育情况和实验室内强度发育结果吻合度相差较大的情况,按照该井区耐高温高压超高密度水泥浆体系配方,在120和160℃下,分别模拟井下实际压力和GB/T 19139-2012中要求的20.7 MPa压力下进行水泥试块的制备,开展常温抗压强度、抗折强度、单轴压缩实验以及井下温度下的三轴压缩实验,探究压力对超高密度水泥石抗压强度、抗折强度的影响以及试块的变形、破坏模式等力学特征。实验结果表明,压力是超高密度水泥石早期强度发展的关键因素之一;随着养护压力的增加,超高密度水泥试块的顶部抗压强度增加61.53%、底部抗压强度增加了120%;顶部抗折强度增加了65.2%,底部抗折强度增加了62.8%;常温下单轴压缩实验水泥石表现出明显的弹脆特性,在20.7 MPa下养护后试块端部出现明显破损,随着养护压力的增加,试块的峰值应力和弹性模量增加,抵抗变形破坏的能力增强;高温下的三轴压缩实验表明,超高密度水泥石的各项力学参数比单轴情况下均有较大提高,试块的变形均以轴向压缩变形为主,未形成明显的宏观裂纹,体现出良好的抵抗破坏变形的能力,更加接近线弹性-理想塑性材料。建议室内实验检测和模拟方法应充分考虑实际井况条件对水泥石力学性能的影响。
The south rim of the Junggar Basin is a key block for reserve increase of the Xinjiang oilfield. Wells drilled in this area are 6,000-8,000 m in depth, the bottom hole temperature and pressure of which are 160 ℃ and 170 MPa respectively, typical “three high” wells. Studies were conducted on the basic properties of the high temperature high pressure and ultra-high density cement slurries used in this area as well as the mechanical performance of the ultra-high density set cement under high temperature high pressure. In general laboratory studies, the strength development of a cement slurry is always quite different than the strength development of the same cement slurry in field operation. To understand the causes for this phenomenon, set cement test samples made from the typical cement slurry compositions used in this area were tested at 120 ℃ and 160 ℃, respectively under simulated actual downhole pressures and the pressure specified in the standard GB/T 19139-2012, which is 20.7 MPa. The tests include compressive strength test, flexural strength test and uniaxial compression test at room temperatures and triaxial compression test at actual downhole temperatures. Through these tests, the effects of pressure on the compressive strength and flexural strength of ultrahigh density set cement, as well as the mechanical characteristics(deformation, failure mode etc.) of the set cement samples were investigated. The test results showed that pressure is one of the key factors affecting the development of the early strength of ultrahigh density set cement. As the curing pressure increases, the compressive strengths of the top and bottom of the set cement were increased by 61.53% and 120%, respectively, the flexural strength of the top and bottom of the set cement were increased by 65.2%and 62.8%, respectively. Set cement tested in uniaxial compressive test at room temperatures showed obvious brittleness. After curing under 20.7 MPa, the ends of the set cement samples were obviously damaged. As the curing pressure was increased, the peak stress and elastic modulus were both increased, and the ability of the set cement samples to resist deformation failure was improved.High temperature triaxial compression test results showed that all mechanical parameters of ultra-high density set cement were greatly increased compared with the mechanical parameters obtained in uniaxial compression test, and the deformation of the set cement was mainly in a form of axial compression deformation, no obvious macro cracks were ever developed in the set cement,indicating that the set cement performed very well in resisting deformation failure, and was more like a linear-elastic – ideal plastic material. It is suggested that in laboratory examination and simulation experiment, the effects of actual downhole conditions on the mechanical performance of set cement be taken into account.
作者
宋鹤
杨威
唐俊峰
刘翠微
王敬朋
林志伟
SONG He;YANG Wei;TANG Junfeng;LIU Cuiwei;WANG Jingpeng;LIN Zhiwei(CNPC Engineering Technology Research Co.,Ltd.,Tianjin 300450;Engineering Technology Research Institute of Xinjiang Oilfield,Karamay,Xinjiang 834000)
出处
《钻井液与完井液》
CAS
北大核心
2021年第6期771-777,共7页
Drilling Fluid & Completion Fluid
基金
中国石油天然气集团有限公司重大技术现场试验“准噶尔南缘和玛湖等重点地区优快钻完井技术集成与实验”(2019F-33)。
关键词
高温
高压
超高密度
水泥石
力学性能
实际井况
超高压力养护
High temperature
High pressure
Ultra-high density
Set cement
Mechanical performance
Actual downhole condition
Cure under ultra-high pressure