摘要
Controlling of the solution and precipitation for microalloying additions of Nb,V,Ti and their combination is the basic building block of microalloyed steels.Among three microalloying elements,Nb has been regarded the most effective microalloying ingredient used for low carbon flat products due to marked strengthening effect of grain refinement and relatively weak precipitation strengthening effect by matching proper thermomechanical processing(TMP).However,Nb was not viewed as attractive as V for medium carbon long products in the past because of limited solubility during reheating process.What is more,hot working is usually carried out at high temperatures in the recrystallization regime,so it is difficult to exert conventional controlled rolling to obtain pancaked austenite,which has further affected the research and application of Nb in medium carbon long products.Because of these factors,studies of Nb in medium carbon long products were incomplete,and even some recognitions and conclusions are subjected to debate.In order to clarify the strengthening effects of Nb in medium carbon long products,the reinforcing bars have been chosen as experimental steels to clarify the role of Nb on microstructural changes along the whole hot working,cooling processes.In addition,qualitative and quantitative analyses of Nb’s state and distribution in reheating,rolling and cooling had been carried out to illustrate some singularities.