3D Printing of Polylactic Acid Bioplastic–Carbon Fibres and Twisted Kevlar Composites Through Coextrusion Using Fused Deposition Modeling

Polylactic acid(PLA)bioplastic is a common material used in Fused Deposition Modeling(FDM)3D printing.It is biodegradable and environmentally friendly biopolymer which made out of corn.However,it exhibits weak mechanical properties which reduced its usability as a functional prototype in a real-world application.In the present study,two PLA composites are created through coextruded with 3K carbon fibres and twisted Kevlar string(as core fibre)to form a fibre reinforced parts(FRP).The mechanical strength of printed parts was examined using ASTM D638 standard with a strain rate of 1 mm/min.It has been demonstrated that the FRPs coextruded with 3K carbon fibres had achieved significant improvement in Young’s modulus(+180.6%,9.205 GPa),ultimate tensile strength(+175.3%,103 MPa)and maximum tensile strain(+21.6%,1.833%).Although the Young’s modulus of Kevlar FRP was found to be similar to as compared to unreinforced PLA(~3.29 GPa),it has gained significant increment in terms of maximum tensile strain(+179.7%,104.64 MPa),and maximum tensile strain(+257%,5.384%).Thus,this study revealed two unique composite materials,in which the 3K carbon FRP can offer stiff and high strength structure while Kevlar FRP offers similar strength but at a higher elasticity.