摘要
Magnesium alloys are used in aircraft because of their light weight.However,for these alloys to be applied in electronic devices,high thermal conductivities are required.Several high-potential compositions of Mg-Zn-Y-Zr alloys were selected by phase composition and their freezing ranges calculated using Thermo-Calc software.The alloys were prepared,and their fluidity,hot tearing susceptibility,mechanical properties,and thermal conductivity were obtained and compared.The alloy composed of Mg-4 wt%Zn-3 wt%Y-0.3 wt%Zr was selected for further investigation,because of its high thermal conductivity and satisfactory mechanical properties.The Mg-4 wt%Zn-3 wt%Y-0.3 wt%Zr alloy’s fluidity and hot tearing susceptibility were similar to those of the widespread AZ91 commercial casting magnesium alloy.The influence of a heat treatment regime on the microstructure,thermal conductivity,and mechanical properties of the developed alloy was also investigated.It was established that the room temperature thermal conductivity of the Mg-4 wt%Zn-3 wt%Y-0.3 wt%Zr alloy after aging at 300℃for 5 h was 105 W/m K^(-1).Additionally,the following tensile test results were obtained in aged condition:120 MPa yield strength,200 MPa ultimate tensile strength,and 4%elongation.The utilization of solid solution heat treatment at 520℃for 8 h prior to aging can promote up to 9%increase in elongation.The Mg-4 wt%Zn-3 wt%Y-0.3 wt%Zr casting alloy can be used as a high thermal conductivity material with industrial applications.