Synchrotron Characterisation of Ultra-Fine Grain TiB_(2)/Al-Cu Composite Fabricated by Laser Powder Bed Fusion

Isotropy in microstructure and mechanical properties remains a challenge for laser powder bed fusion(LPBF)processed materials due to the epitaxial growth and rapid cooling in LPBF.In this study,a high-strength TiB_(2)/Al-Cu composite with random texture was successfully fabricated by laser powder bed fusion(LPBF)using pre-doped TiB_(2)/Al-Cu composite powder.A series of advanced characterisation techniques,including synchrotron X-ray tomography,correlative focussed ion beam-scanning electron microscopy(FIB-SEM),scanning transmission electron microscopy(STEM),and synchrotron in situ X-ray diffraction,were applied to investigate the defects and microstructure of the as-fabricated TiB_(2)/Al-Cu composite across multiple length scales.The study showed ultra-fine grains with an average grain size of about 0.86μm,and a random texture was formed in the as-fabricated condition due to rapid solidification and the TiB_(2)particles promoting heterogeneous nucleation.The yield strength and total elongation of the as-fabricated composite were 317 MPa and 10%,respectively.The contributions of fine grains,solid solutions,dislocations,particles,and Guinier-Preston(GP)zones were calculated.Failure was found to be initiated from the largest lack-of-fusion pore,as revealed by in situ synchrotron tomography during tensile loading.In situ synchrotron diffraction was used to characterise the lattice strain evolution during tensile loading,providing important data for the development of crystal-plasticity models.