Herein,a series of niobium oxide supported cerium nanotubes(Ce NTs)catalysts with different loading amount of Nb_(2)O_(5)(0–10 wt.%)were prepared and used for selective catalytic reduction of NOxwith NH_(3)(NH_(3)-SCR)in the presence of CH_(2)Cl_(2).Commercial V_(2)O_(5)-WO_(3)-TiO_(2) catalyst was also prepared for comparison.The physcial properties and chemical properties of the Nb_(2)O_(5) loaded cerium nanotubes catalysts were investigated by X-ray diffractometer,Transmission electron microscope,Brunauer-Emmett-Teller specific surface area,H_(2)-temperature programmed reduction,NH_(3)-temperature programmed desorption and Xray photoelectron spectroscopy.The experiment results showed that the loading amount of Nb_(2)O_(5) had a significant effect on the catalytic performance of the catalysts.10 wt.%Nb-Ce NTs catalyst presented the best NH_(3)-SCR performance and degradation efficiency of CH_(2)Cl_(2) among the prepared catalysts,due to its superior redox capability,abundant surface oxygen species and acid sites,the interaction between Nb and Ce,higher ratio of Nb^(4+)/(Nb^(5+)+Nb^(4+))and Ce^(3+)/(Ce^(3+)+Ce^(4+)),as well as the special tubular structure of cerium nanotube.This study may provide a practical approach for the design and synthesis of SCR catalysts for the simultaneously removal NOxand chlorinated volatile organic compounds(CVOCs)emitted from the stationary industrial sources.
基金
financially supported by National Natural Science Foundation of China(Nos.52070168 and 51708492)
National Key Research and Development Plan of China(No.2016YFC0204100)
Zhejiang Provincial“151 Talents Program
the Program for Zhejiang Leading Team of S&T Innovation(No.2013TD07)。