摘要
Copper ion conducting solid electrolyte Rb_(4)Cu_(16)I_(6.5)Cl_(13.5)was prepared by means of mechano-chemical method.The structure and morphology of the powder was investigated by x-ray diffraction and scanning electron microscopy.The grain size was estimated to be 0.2-0.9μm and the ionic conductivity at room temperature was approximately 0.206 S/cm.The solid electrolyte Rb_(4)Cu_(16)I_(6.5)Cl_(13.5)was exploited for copper ion beam generation.The copper ion emission current of several nA was successfully obtained at acceleration voltages of 15 kV and temperature of 197℃in vacuum of 2.1×10^(-4)Pa.A good linear correlation between the logarithmic ion current(logI)and the square root of the acceleration voltage(U_(acc))at high voltage range was obtained,suggesting the Schottky emission mechanism in the process of copper ion beam generation.
作者
吐沙姑·阿不都吾甫
张翔宇
左文彬
罗进宝
兰越强
田灿鑫
邹长伟
Alexander Tolstoguzov
付德君
Tushagu Abudouwufu;Xiangyu Zhang;Wenbin Zuo;Jinbao Luo;Yueqiang Lan;Canxin Tian;Changwei Zou;Alexander Tolstoguzov;Dejun Fu(Key Laboratory of Artificial Micro and Nanostructures of Ministry of Education and Hubei Key Laboratory of Nuclear Solid Physics,School of Physics and Technology,Wuhan University,Wuhan 430072,China;Shenzhen Institute of Wuhan University,Shenzhen 518057,China;Zhuhai Tsinghua University Research Institute Innovation Center,Zhuhai 519000,China;School of Physics and Technology,Lingnan Normal University,Zhanjiang 524048,China;Utkin Ryazan State Radio Engineering University,Ryazan 390005,Russian Federation)
基金
supported by Shenzhen Municipal Science and Technology Innovation Commission(Grant Nos.JCYJ20170818112901473 and GJHZ20200731095604015)
the Department of Science and Technology of Guangdong Province,China(Grant Nos.2020A0505100059,2020A1515011531,and 2020A1515011451)
by the Ministry of Education and Science of the Russian Federation in the frame of the state assignment(Grant No.FSSN-2020-0003)。