摘要
The strengthening mechanisms of Al-TiAl_(3) nanocomposite, fabricated using cold roll bonding, annealing, and accumulative roll bonding(ARB) on Al sheets sandwiching with pure Ti powder were investigated in the present study. With annealing at 590 ℃ for 2 h, TiAl_(3) intermetallic compound was formed. After subsequent ARB process up to 5 cycles, final composite consists of ultrafine Al grains of less than 500 nm with TiAl_(3) particles larger than 200 nm. The strength and hardness of the final composite are 2.5 and 3.5 times the initial values, with an ultimate tensile strength of 400 MPa, which is dominated by grain-boundary strengthening due to the ultrafine Al grains, and Orowan strengthening due to the small TiAl_(3) particles. For comparison, an alternative fabrication route of cold roll bonding–ARB–annealing was also studied. This study showed that annealing before ARB is a critical factor in producing an ultrafine grain structure containing TiAl_(3) particles.