摘要
The novel and facile preparation of magnetically interconnected micro/macroporous structure of monolithic porous carbon adsorbent(MPCA)were designed and presented herein.The synthesis was achieved via conventional freezedrying and pyrolysis processes.In this study,sodium alginate and wasted black liquor were employed as starting precursors.Sodium alginate acts as a template of materials,whereas black liquor,the wasted product from the paper industry with plentiful of lignin content and alkaline solution,played an essential role in the reinforcement and activation of porosity for the resulting materials.Moreover,both the precursors were well dissolved in Fe^(3+) solution,providing a simple addition of a magnetic source in a one-pot synthesis.The interconnected micro/macroporous structures were generated through freeze-drying and,subsequently the pyrolysis process.The obtained cylindricalshaped monolithic porous carbon adsorbent(MPCA-700)showed high mechanical stability,a high BET specific surface area(902 m^(2)/g).Such aforementioned features were considered suitable to make the synthesized monolith as an adsorbent for the removal of heavy metal ions.The maximum adsorption capacity of MPCA-700 towards Pb^(2+) ions was 76.34 mg/g at pH 5.The adsorption studies illustrated that adsorption kinetics and isotherm perfectly fitted with the pseudo-second-order kinetics model and Langmuir isotherm,respectively.This work presents a promising protocol to reduce the overall costs in the preparation of renewable adsorbents with good adsorption efficiency and regeneration.
基金
This work was funded by Development and Promotion of Science Technology Talents(DPST)Research Grant(Grant No.017/2559)
the Institute for the Promotion of Teaching Science and Technology(IPST),Thailand.