磷化镍@镍-氮-碳双功能催化剂电还原CO_(2)-H_(2)O制合成气 被引量:5

Engineering of Bifunctional Nickel Phosphide@Ni-N-C Catalysts for Selective Electroreduction of CO_(2)-H_(2)O to Syngas
下载PDF
导出
摘要 电催化还原CO_(2)由于具有温和的反应条件、反应产物组成可调、环境友好等优点,是CO_(2)转化技术中最有前景的方法之一,然而目前发展的电催化CO_(2)还原技术仍未达到工业化盈利所需的技术经济指标。因此,通过简单的两电子转移,将CO_(2)-H_(2)O电还原为合成气通常被认为是电化学还原CO_(2)过程中较有前景的实现盈利的途径之一,因此研究能够精确调控合成气比例的非贵金属电催化剂至关重要。在本文中,我们提出了通过三元纳米复合材料的分子工程学设计的进行了高活性、可实现特定比例合成气制备的双功能电催化剂的合成策略。将三聚氰胺、三苯基膦(TPP)和乙酸镍研磨并溶解在乙醇中,通过旋蒸得到三元纳米复合材料,在850℃下热解2 h得到催化剂。该方法简单、易操作并且易于放大。该系列双功能电催化剂的比表面积和孔体积均随着三苯基膦量的增加而增加,且分级孔结构有利于提供活性位以及促进物质传输。此外,拉曼图谱表明材料的缺陷度由于前驱体中三苯基膦的增加而增加。另外,X射线光电子能谱验证了析氢反应活性位点Ni-P和CO_(2)电催化活性为位点Ni-N的存在。因此,该系列电催化剂的性能具有较大的调控空间,可从CO产物主导调控至H_(2)产物主导。电化学性能通过在CO_(2)饱和0.5 mol·L^(-1) KHCO_(3)溶液中进行线性扫描伏安法以及恒电位电解进行评价。结果表明催化剂的活性受材料表面P/Ni-N_(x)比例的影响。最高的CO法拉第效率为91%,由不含磷化镍的纯Ni-N-C材料在−0.8 V(相对于可逆氢电极(RHE))电位下实现。在−0.7至−1.1 V(vs RHE)电位区间内,合成气流中CO/H_(2)的摩尔比可从2:5调整至10:1,并能与磷化镍和镍-氮-炭组分的摩尔比关联。此外,我们还对优化的催化剂在−0.7 V电位下的稳定性进行了测试,合成气摩尔比例在8 h内保持在1.2–1.3,说明材料具有良好的稳定性。本工作将温室气体CO_(2)和H_(2)O转化成比例可调的合成气,为双功能电催化剂的工程设计提供了新的方向。 Electroreduction of CO_(2) is one of the most promising CO_(2) conversion pathways because of its moderate reaction conditions,controllable product composition,and environment-friendliness.However,most of the current CO_(2) electroreduction technologies have not reached the techno-economic threshold for a competitively profitable electrochemical process.Based on a simple two-electron transfer process,the electroreduction of CO_(2) to CO,which is further processed into syngas with the reduction of H_(2)O to H_(2),is postulated to be the most promising pathway for a profitable electrochemical process.Such a process urgently requires nonprecious electrocatalysts that can precisely control the CO/H_(2) ratio.Herein,we present a tailored synthesis of bifunctional electrocatalysts with high activity,which can realize the preparation of syngas with controlled compositions via molecular engineering of a ternary nanocomposite.Specifically,a mixture of melamine,triphenylphosphine,and nickel acetate was milled and dissolved in ethanol;the ternary nanocomposite was obtained after rotary evaporation of the mixture.We prepared the catalysts by pyrolyzing the obtained composites at 850℃ for 2 h.The synthesis strategy was facile and easy to scale.The specific surface area and pore volume of the bifunctional electrocatalyst were both significantly enhanced upon increasing the concentration of the phosphorus source,triphenylphosphine,during the precursor preparation.The obtained bifunctional electrocatalysts had hierarchically porous structures,which had well-dispersed active sites and could promote mass transport.Raman spectra revealed higher degrees of disorder with higher P/Ni ratios in the precursor.X-ray photoelectron spectroscopy verified the presence of Ni-P_(x) and Ni-N_(x) functionalities,which were the active sites for hydrogen evolution and CO_(2) reduction,respectively.Hence,the electrocatalytic performance of this series of bifunctional electrocatalysts can be tuned from CO-dominant to H_(2)-dominant.The electrochemical performance was evaluated using a CO_(2)-saturated 0.5 mol·L^(-1) KHCO_(3) aqueous solution at ambient temperature by linear sweep voltammetry and potentiostatic electrolysis.Through these experiments,we determined that the activity of the catalysts was influenced by the surface phosphorus/NiN_(x) site ratio.The highest CO faradaic efficiency(91%)was achieved at−0.8 V(vs a reversible hydrogen electrode,RHE)with Ni-N-C in the absence of Ni-P.The CO/H_(2) molar ratio in the syngas stream was tunable from 2:5 to 10:1 in the potential range from−0.7 to−1.1 V(vs RHE)with a total faradic efficiency of 100%.The syngas composition directly links to the molar ratio of the two integrated components,nickel phosphide and Ni-N-C.Additionally,the stability of the optimized bifunctional electrocatalyst at−0.7 V for 8 h was tested,in which the CO/H_(2) ratio was maintained between 1.2 and 1.3,indicating excellent stability.This study provides a new perspective for the engineering of bifunctional electrocatalysts for the conversion of abundant CO_(2) and water into syngas with tailorable CO/H_(2) ratios.
作者 叶成玉 郁晓菲 李文翠 贺雷 郝广平 陆安慧 Chengyu Ye;Xiaofei Yu;Wencui Li;Lei He;Guangping Hao;Anhui Lu(State Key Laboratory of Fine Chemicals,Liaoning Key Laboratory for Catalytic Conversion Carbon Resources,School of Chemical Engineering,Dalian University of Technology,Dalian 116024,Liaoning Province,China)
出处 《物理化学学报》 SCIE CAS CSCD 北大核心 2022年第4期92-102,共11页 Acta Physico-Chimica Sinica
基金 国家自然科学基金(21975037) 长江学者奖励计划(T2015036) 中央高校基本科研业务费专项资金(DUT18RC(3)075) 辽宁振兴人才计划(XLYC1807205)资助项目
关键词 非贵金属催化剂 CO_(2)电还原 合成气 多孔碳 磷化镍 Nonprecious catalyst CO_(2)electroreduction Syngas Porous carbon Nickel phosphide