The effectiveness of Ca or Gd addition on ductility and formability of Mg-Zn-Zr based dilute alloys in deep drawing has not been systematically compared previously.In this study,formable Mg-Zn-Gd-Zr and Mg-Zn-Ca-Zr sheet alloys are produced by hot rolling.These sheets have similarly weakened basal texture,but the sheet of the Mg-Zn-Gd-Zr alloys has higher ductility and formability than that of Mg-Zn-Ca-Zr alloys.The combined addition of 0.2wt%Ca and 0.4wt%Gd to the Mg-1Zn-0.5Zr(wt%)alloy leads to a Mg-1Zn-0.4Gd-0.2Ca-0.5Zr alloy that has even better ductility,and its formability during deep drawing is comparable to the benchmark Al6016 sheet.An increase in Ca content from 0.2wt%to 0.5wt%leads to decreased sheet ductility and formability,predominantly due to grain boundary embrittlement.