在强度为6 T的磁场中,在不同温度下,对真空热压成型的钌进行热处理,测定了样品的硬度和密度,并进行了X射线衍射(XRD)织构分析和扫描电镜(SEM)表征。结果表明,经强磁场热处理后钌的密度无变化,硬度增大;在强磁场和热处理温度的的共同作用下,钌内部原子迁移,从而使其晶粒取向、织构分布发生改变。
Ruthenium sintered by vacuum hot pressing was further heat-treated at different temperatures in a 6 T strong magnetic field.The hardness and density of Ru were measured.XRD,SEM were used to analyze the texture and structure of Ru before and after treatment.The results showed that the density had no change,and that its hardness increased after treatment.Due to the influence of the strong magnetic field and heat treatment,the migration of atoms inside the sample changes the grain orientation and texture distribution of Ru.
作者
甘俊
张仁耀
裴文利
周利民
闻明
GAN Jun;ZHANG Ren-yao;PEI Wen-li;ZHOU Li-min;WEN Ming(Kunming Institute of Precious Metals,State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino Platinum Metals Co.Ltd.,Kunming 650106,China;School of Materials Science and Engineering,Northeastern University,Shenyang 110006,China)
出处
《贵金属》
CAS
北大核心
2022年第1期34-38,共5页
Precious Metals
基金
国家重点研发计划项目(2017YFB0305503)
云南省创新团队项目(2019HC024)
云南省基金青年项目(2019FD140)
云南省重大科技专项(202102AB080008-4)。
关键词
金属材料
钌靶材
热处理
强磁场
织构
metal materials
ruthenium target material
heat treatment
strong magnetic field
texture