Self-assembled donor-acceptor hole contacts for inverted perovskite solar cells with an efficiency approaching 22%: The impact of anchoring groups

Self-assembled molecules(SAMs) have shown great potential in replacing bulk charge selective contact layers in high-performance perovskite solar cells(PSCs) due to their low material consumption and simple processing. Herein, we design and synthesize a series of donor-acceptor(D-A) type SAMs(MPA-BTCA, MPA-BT-BA, and MPA-BT-RA, where MPA is 4-methoxy-N-(4-methoxyphenyl)-N-phenylaniline;BT is benzo[c][1,2,5]-thiadiazole;CA is 2-cyanoacrylic acid, BA is benzoic acid, RA is rhodanine-3-propionic acid) with distinct anchoring groups, which show dramatically different properties. MPA-BTCA with CA anchoring groups exhibited stronger dipole moments and formed a homogeneous monolayer on the indium tin oxide(ITO) surface by adopting an upstanding self-assembling mode. However, the MPA-BT-RA molecules tend to aggregate severely in solid state due to the sp~3 hybridization of the carbon atom on the RA group, which is not favorable for achieving a long-range ordered self-assembled layer.Consequently, benefiting from high dipole moment, as well as dense and uniform self-assembled film,the device based on MPA-BT-CA yielded a remarkable power conversion efficiency(PCE) of 21.81%.Encouragingly, an impressive PCE approaching 20% can still be obtained for the MPA-BT-CA-based PSCs as the device area is increased to 0.80 cm^(2). Our work sheds light on the design principles for developing hole selecting SAMs, which will pave a way for realizing highly efficient, flexible, and large-area PSCs.