摘要
The separator with excellent mechanical and thermal properties are highly required for lithium ion batteries(LIBs).Therefore,it is crucial to develop novel nanofbrous membranes with enhanced mechanical strength and thermal stability.In this work,the fuorinated polyimide(FPI)was synthesized and blended with polyvinylidene fuoride(PVDF)to fabricate composite nanofbrous membranes(CNMs)via electrospinning method.Benefting from the introduction of aromatic FPI,the prepared PVDF/FPI nanofbrous membranes were endowed with enhanced mechanical strength and thermal stability.When the FPI content increased from 0 to 30 wt%,the tensile strength of composite nanofbrous membranes enhanced from 1.57 to 2.30 MPa.Moreover,there are almost no dimensional shrinkage for the CNM-30 containing 30 wt%FPI after heat treatment at 160℃ for 1 h.Furthermore,the prepared CNMs show improved electrochemical performances in comparison with neat PVDF and commercial Celgard membranes.The electrolyte uptake and ionic conductivity of the CNMs could reach to 522.4% and 1.14 ms·cm^(−1),respectively.The prepared CNMs could provide an innovative and promising approach for the development and design of high-performance separators.
基金
The authors gratefully acknowledge the supports from the Emergency Support and Public Safety Scientifc Research Projects of National Advanced Functional Fiber Innovation Center(2020-fx020009)
The Postgraduate Innovation Foundation of Xi’an Polytechnic University(CHX2020037)
Natural Science Foundation of Education Department of Shaanxi Province(21JK0657).