Non-toxic rare earth(RE) composite materials are promising and active in optoelectronic fields,such as pigment.In this work,Na ions doped γ-Ce_(2) S_(3) pigments were synthesized by solid-phase vulcanization and followed by in-situ synthesis to prepare an outer layer of CePO_(4) film.The characterizations of X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),X-ray photoelectron spectroscopy(XPS),solid state nuclear magnetic resonance(NMR) indicate that Na-dopedγ-Ce_(2) S_(3) and CePO_(4) uniformly and tightly coated core-shell structure was successfully synthesized.The thermogravimetric analysis(TG) and reflection spectrum(RS) reveal that the CePO_(4) coating significantly improves the colorant and thermal stability performance of γ-Ce_(2) S_(3) .The excellent color quality of γ-Ce_(2) S_(3) @CePO_(4)(L*=45.16,a*=55.94.b*=44.53) is achieved and the red color(L*=43.82,a*=49.79,b*=38.04) is still retained even if the sample is heated in air at 400℃ for 30 min.
基金
Project supported by the Natural Science Foundation of Zhejiang Province,China(LQ21E020006)
the National Key Research and Development Program of China(2019YFA0709101)
Opening Fund of State Key Laboratory of Rare Earth Resource Utilization,China(Changchun Institute of Applied Chemistry)(RERU2018012)。