Hot compressive deformation of eutectic Al-17at%Cu alloy on the interface of the Cu-Al composite plate produced by horizontal continuous casting

On the interface of the Cu-Al composite plate from horizontal continuous casting,the eutectic microstructure layer thickness ac-counts for more than 90%of the total interface thickness,and the deformation in rolling forming plays an important role in the quality of the composite plate.The eutectic microstructure material on the interface of the Cu-Al composite plate was prepared by changing the cooling rate of ingot solidification and the deformation in hot compression was investigated.The results show that when the deformation temperature is over 300℃,the softening effect of dynamic recrystallization ofα-Al is greater than the hardening effect,and uniform plastic deformation of eutectic microstructure is caused.The constitutive equation of flow stress in the eutectic microstructure layer was established by Arrhenius hy-perbolic-sine mathematics model,providing a reliable theoretical basis for the deformation of the Cu-Al composite plate.