Thermal barrier coating(TBC)materials perform an increasingly important role in the thermal or chemical protection of hot components in a gas turbine.In this study,a novel high entropy hafnate(Y_(0.2)Gd_(0.2)Dy_(0.2)Er_(0.2)Yb_(0.2))_(2)Hf_(2)O_(7) was synthesized by solution combustion method and investigated as a potential TBC layer.The as-synthesized(Y_(0.2)Gd_(0.2)Dy_(0.2)Er_(0.2)Yb_(0.2))_(2)Hf_(2)O_(7) possesses a pure single disordered fluorite phase with a highly homogeneous distribution of rare earth(RE)cations,exhibiting prominent phase stability and excellent chemical compatibility with Al_(2)O_(3) even at 1300°C.Moreover,(Y_(0.2)Gd_(0.2)Dy_(0.2)Er_(0.2)Yb_(0.2))_(2)Hf_(2)O_(7) demonstrates a more sluggish grain growth rate than Y_(2)Hf_(2)O_(7).The thermal conductivity of(Y_(0.2)Gd_(0.2)Dy_(0.2)Er_(0.2)Yb_(0.2))_(2)Hf_(2)O_(7)(0.73-0.93 W m^(-1)K^(-1))is smaller than those of components RE_(2)Hf_(2)O_(7) and many high entropy TBC materials.Beside,the calculated thermal expansion coefficient(TEC)of(Y_(0.2)Gd_(0.2)Dy_(0.2)Er_(0.2)Yb_(0.2))_(2)Hf_(2)O_(7)(10.68×10^(-6)/K,1100°C)is smaller than that of yttriastabilized zirconia(YSZ).Based on the results of this work,(Y_(0.2)Gd_(0.2)Dy_(0.2)Er_(0.2)Yb_(0.2))_(2)Hf_(2)O_(7) is suitable for the next generation TBC materials with outstanding properties.
基金
financially supported by the National Natural Science Foundation of China (Nos. 51872234, 51502242, 51432008, 51802244, and 51821091)
the Key R&D Program of Shaanxi Provence (No. 2019ZDLGY04-02)。