The commercialisation of molten salts reactors(MSRs)is hindered by the lack of structural materials capable of withstanding the corrosive environment therein.To address this problem,we herein prepared1 wt%Y_(2)O_(3)mdispersion-strengthened Ni Mo-based alloys using powder metallurgy and evaluated their potential as structural materials for MSRs based on their mechanical properties,He swelling behaviour,and molten salt corrosion resistance.In view of the strengthening provided by homogenously dispersed Y_(2)O_(3)particles,all NiMo-Y_(2)O_(3)samples exhibited ultimate tensile strengths and yield strengths exceeding those of the Hastelloy N alloy,a state-of-the-art structural material for MSRs.Moreover,the volume fraction of He bubbles in the NiMo-Y_(2)O_(3)samples(~0.3%)was lower than that in the Hastelloy N alloy(0.58%),which showed that the introduction of Y_(2)O_(3)nanoparticles effectively inhibited He swelling.All NiMo-Y_(2)O_(3)samples showed excellent resistance to molten salt corrosion(as reflected by the absence of obvious holes therein),thus holding great promise for the development of irradiation-and molten salt corrosion-resistant structural materials for high-temperature MSRs.
基金
supported by the National Natural Science Foundation of China(Grant Nos.11975304,12022515,11805261,11805256)
Youth Innovation Promotion Association,Chinese Academy of Sciences(Grant No.Y202063)。