摘要
The NaNbO_(3) antiferroelectrics have been considered as a potential candidate for dielectric capacitorsapplications. However, the high-electric-field-unstable antiferroelectric phase resulted in low energystorage density and efficiency. Herein, good energy storage properties were realized in (1-x)NaNbO_(3)- xNaTaO_(3) ceramics, by building a new phase boundary. As a result, a high recoverable energy density(Wrec) of 2.2 J/cm3 and efficiency (h) of 80.1% were achieved in 0.50NaNbO_(3)-0.50NaTaO_(3) ceramic at300 kV/cm. The excellent energy storage performance originates from an antiferroelectric-paraelectricphase boundary with simultaneously high polarization and low hysteresis, by tailoring the ratio ofantiferroelectric and paraelectric phases. Moreover, the 0.50NaNbO_(3)-0.50NaTaO_(3) ceramic also exhibitedgood temperature and frequency stability, together with excellent charge-discharge performance. Theresults pave a good way of designing new NaNbO_(3)-based antiferroelectrics with good energy storageperformance.
基金
This work was financially supported by the National Natural Science Foundation of China(Grant Nos.11864004 and 52072080)
The author also thanks to the fund(Grant No.20KF-16)from the Key Laboratory of New Processing Technology for Nonferrous Metal&Materials,Ministry of Education/Guangxi Key Laboratory of Optical and Electronic Materials and Devices,Guilin University of Technology,Guilin(541004),China.