摘要
Zirconia(ZrO_(2))ceramics have potential applications in the field of oral medicine owing to their desirable me-chanical properties,biocompatibility,chemical stability,and aesthetic properties.To realize clinical applications,ZrO_(2)(3Y)/Al_(2)O_(3)bioceramics for all-ceramic dental implants were prepared using vat photopolymerization 3D printing technology,and their process optimization,microstructure,mechanics,tribology,and biological proper-ties were studied.The results indicate that when the sintering temperature and holding time are 1600℃and 3 h,respectively,the density of ZrO_(2)(3Y)/Al_(2)O_(3)bioceramics reaches 98.79%,and its Vickers hardness,compressive strength,flexural strength,and fracture toughness also reach their maximum values.Furthermore,the in vitro sim-ulated oral environment wear tests showed that artificial saliva provides a lubricating effect on ZrO_(2)(3Y)/Al_(2)O_(3)bioceramics and improves wear resistance.The biosafety of ZrO_(2)(3Y)/Al_(2)O_(3)bioceramics was evaluated and ZrO_(2)(3Y)/Al_(2)O_(3)had no obvious cytotoxicity and promoted cell proliferation,growth,and adhesion.In addition,its surface has appropriate roughness and good wettability.In conclusion,ZrO_(2)(3Y)/Al_(2)O_(3)bioceramics prepared by vat photopolymerization are promising biomaterials with broad application prospects in dental restoration.
基金
supported by Beijing Municipal Science and Tech-nology Project(Grant No.KM202010005003)
General Program of Science and Technology Development Project of the Beijing Municipal Education Commission.