A series of compositionally complex fluorite oxides(CCFOs)were prepared by ball milling the mixture of ZrO_(2),HfO_(2),Y_(2)O_(3),La_(2)O_(3),and Pr_(6)O_(11)followed by conventional solid-state sintering.Both XRD and TG-DSC results demonstrated that single-phase(Zr_(0.2)Hf_(0.2)Pr_(0.2)Y_(0.2)La_(0.2))O_(2-)δwas formed at 1400°C.Elements in bulk ceramic were uniformly distributed without evident accumulation according to SEM-EDS pictures.TEM results revealed that polycrystalline ceramic powder was assignable to cubic Fm-3m fluorite structure.The electrical conductivity(σ)was measured via EIS technology and activation energy(E_(a))of CCFOs was calculated in Arrhenius plots.In the temperature range of 300-750°C,CCFOs preserved the same conduction mechanism and(Zr_(0.1667)Hf_(0.1667)Pr_(0.1667)Y_(0.25)La_(0.25))O_(2-)δpossessed higherσand lower E_(a) than other high entropy fluorite oxides which is related to the incorporation of Pr element or the connection of cation-V_(o) complex.
基金
supported by National Natural Science Foundation for Young Scientists of China(Grant No.51802213)
National Natural Science Foundation of China(Grant Nos.U1710256 and 52072256)
Program of Applied Basic Research Program of Shanxi Province(Grant No.201901D211118)。