In this paper,the effect of Ba^(2+)ions A-site doping LaFeO_(3)on structure,magnetic properties and microwave absorption properties was investigated by the sol-gel method.According to the TEM and FullProf refinement results,the structure of LaFeO_(3)changes from orthogonal(SG:Pnma)to cubic(SG:Pm-3 m)when the Ba doping amount is x=0.4.The SEM image shows that the particles size tends to decrease with the increase of Ba content.The production of weak ferromagnetism indicates that Ba doping has a significant effect on the magnetic properties of LaFeO_(3).The Neel temperature(TN)decreases significantly with the increase of Ba doping amount.An appropriate amount of Ba doping can effectively increase the dielectric and magnetic loss of LaFeO_(3)ceramics powders.The increase permittivity(ε’andε″)may be attributed to the hopping of the electrons between the Fe^(3+)and Fe^(4+)ions with the Ba^(2+)ions doping.The minimum reflection loss(RL_(min))of La_(0.9)Ba_(0.1)FeO_(3)at 6.72 GHz reaches-30.04 dB,its effective bandwidth(RL≤-10 dB)is 2.1 GHz,and the matching thickness is only 3.2 mm.These results indicate that Ba doping can effectively control the microwave absorption properties of LaFeO_(3),especially in the Cband.
基金
Project supported by the National Natural Science Foundation of China(51871066)
Innovation Project of GUET Graduate Education(2020YCXS115)
Guangxi Key Laboratory of Wireless Wideband Communication and Signal Processing(GXKL06170107)
Talents Project of Guilin University of Electronic Technology and Guangxi Key Laboratory of Information Materials(201024-Z,191016-K,191010-Z)。