对塑料电镀件在温度循环+铜加速乙酸盐雾(CASS)试验中出现的花斑、点状腐蚀和铜绿3种形式的腐蚀现象进行了简要分析,提出了提高汽车内饰塑料电镀黑铬件耐蚀性的建议。
Three corrosion forms i.e.piebald,pit,and verdigris appearing on the black-chromium-plated parts after temperature cycle test and copper-accelerated acetic acid salt spray(CASS)test were analyzed.Some suggestions were given to improve the corrosion resistance of black-chromium-plated parts applied to automotive interiors.