摘要
To improve the properties of low-carbonization of MgO–C refractories,the introduction of composite additives is an effective strategy.Al_(2)O_(3)–SiC composite powder was prepared from clay using electromagnetic induction heating and carbon embedded methods.Further,the Al_(2)O_(3)–SiC composite powder synthesized by electromagnetic induction heating at 600 A was added into low-carbon MgO–C refractories(4 wt.%)to improve their properties.The results showed that when the addition amount of Al_(2)O_(3)–SiC composite powder is within the range of 2.5–5.0 wt.%,the properties of low-carbon MgO–C samples were significantly improved,e.g.,the apparent porosity of 7.58%–8.04%,the bulk density of 2.98–2.99 g cm-3,the cold compressive strength of 55.72–57.93 MPa,the residual strength after three air quenching at 1100°C of 74.86%–78.04%,and the decarburized layer depth after oxidized at 1400°C for 2 h of 14.03–14.87 mm.Consequently,the idea for the rapid synthesis of Al_(2)O_(3)–SiC composite powder provides an alternative low-carbon MgO–C refractories performance optimization strategy.
基金
This work was financially supported by the National Natural Science Foundation of China(Grant Nos.U20A20239 and U1908227)
the Fundamental Research Funds for the Central Universities(Grant No.N2125002)
the open research fund for State Key Laboratory of Advance Refractories(Grant No.SKLAR202001).