Engineered bamboo has recently received lots of attention of civil engineers and professional researchers due to its better mechanical performance than that of softwood timber.Parallel strand bamboo is one important part of engineered bamboo for its excellent durable performance compared to the laminated veneer bamboo.The required curing temperature in hot-pressing process is usually higher than 120°C to reduce the content of nutri-tional ingredients and hemy cellulose,and to avoid the decay from the environment and insects.Nonetheless,the appearance of engineered bamboo gets darker with the increase of temperature during the hot-pressing process.In order to minimize the color deepening while maintaining the durability,a high-durable parallel strand bamboo(HPSB)with relative high hot-pressing temperature(140°C)was produced and tested.The present study inves-tigates the mechanical performance through tension,compression,shear and bending tests.The experimental behavior of the specimens was identified,including the failure mode and load-displacement relationship.It was demonstrated that the HPSB material had better mechanical performance parallel to grain,making it as a considerable structural material.The average elastic modulus parallel to grain was 14.1 GPa,and the tensile and compressive strengths were 120.7 MPa and 121.0 MPa,respectively.The tension perpendicular to grain should be avoided in the practical application due to the lower strength and elastic modulus.Two stress-strain relationships of tension and compression parallel to grain,including three-linear and quadratic function models,were proposed and compared with the experimental results.The three-linear model was then applied to the finite element model.The finite element analysis using ANSYS software was conducted to validate the feasibility of the constitutive relationship.The quadratic function model showed better agreement with the experimental results,but the three-linear relationship was also precise enough to analyze the bending tests of HPSB material,whereas being less accurate to describe the elastic-plastic compression behavior.
基金
The authors acknowledge funding supported by the Fundamental Research Funds for the Central Universities of China(No.BLX201706)
supported by Major Science and Technology Program for Water Pollution Control and Treatment(No.2017ZX07102-001)
supported by the National Natural Science Foundation of China(Nos.51908038 and 31770602)。