摘要
In this study,the dredged river sediment,soft texture and fine particles,is mixed with other materials and transformed into eco-friendly autoclaved aerated concrete(hereinafter referred to as AAC)blocks.The results indicated the bricks produced under the conditions of 30%–34%dredged river sediment,24%cement,10%quick lime,30%fly ash,2%gypsum and 0.09%aluminum powder with 0.5 water to material ratio,2.2 MPa autoclave pressure and 6 h autoclave time,the average compressive strength of 4.5 MPa and average dry density of 716.56 kg/m³were obtained,the two parameters(strength&density)both met the requirement of national industry standard.At the same time,the contents of dredged river sediment,cement,lime,fly ash,gypsum and aluminum powder were 15%,48%,20%,15%,2%and 0.09%,respectively,and the non-AAC block made of 0.5 water to material ratio,the average compressive strength of 3.1 MPa and average dry density of 924.19 kg/m³were obtained,the two parameters(strength&density)also met the requirement of national industry standard.In addition,the AAC block’s phase composition and morphology were micro-analyzed by SEM and XRD,the main substances in AAC block were found to be tobermorite and CSH,Among them,the chemical bond between Si-O-Si and Al-O-Al is broken,Al-O-Si is regenerated,Al substituted tobermorite with better strength is formed,and the compressive strength of AAC is further improved.
基金
the National Natural Science Foundation of China(NSFC)(Nos.21876025,42177119).