摘要
为满足低合金钢板大单重、特厚规格的市场需求,依托轧制复合工艺开展采用复合连铸板坯生产特厚钢板的试验研究,通过对连铸板坯进行复合组坯及轧制获得特厚钢板。综合试验和分析结果表明,采用轧制复合工艺生产的特厚钢板结合界面复合良好,结合界面区域晶粒发生了充分的再结晶,实现了原子层级的冶金结合;z向(厚度方向)拉伸性能满足Z35要求,局部断面收缩率因结合界面微区存在的带状分布氧化物而偏低。
In order to meet the market demand of low-alloy steel plate with large single weight and ultra-heavy specifications,the experimental study of ultra-heavy steel plate produced by composite continuous casting slab was carried out by the rolling composite process.Ultra-heavy steel plates were obtained through rolling from composite slab.The comprehensive test and analysis show that the interface bonding of ultra-heavy steel plate produced by rolling composite process is good,and metallurgical bonding at atomic level is achieved with the sufficient recrystallization of grain at the bonding interface.The z-direction tensile properties meet the requirements of Z35,but the local reduction of area is low due to the existence of band-distributed oxides at the bonding interface microregion.
作者
王小勇
王华鹏
贾啸林
邹扬
朴学峰
WANG Xiao-yong;WANG Hua-peng;JIA Xiao-lin;ZOU Yang;PIAO Xue-feng(Research Institute of Technology,Shougang Group Co.,Ltd.,Beijing 100043,China;Heavy Plate Department,Shougang Jingtang United Iron and Steel Co.,Ltd.,Tangshan 063210,Hebei,China)
出处
《中国冶金》
CAS
北大核心
2022年第7期98-102,共5页
China Metallurgy
关键词
低合金
连铸板坯
特厚钢板
轧制复合
结合界面
low-alloy
continuous casting slab
ultra-heavy steel plate
rolling composite
bonding interface