Hierarchical porous carbon derived from coal-based carbon foam for high-performance supercapacitors

Hierarchical porous carbon(HPC)from bituminous coal was designed and synthesized through pyrolysis foaming and KOH activation.The obtained HPC(NCF-KOH)were characterized by a high specific surface area(S_(BET))of 3472.41 m^(2)/g,appropriate mesopores with V_(mes)/V_(total)of 57%,and a proper amount of surface oxygen content(10.03%).This NCF-KOH exhibited a high specific capacitance of 487 F/g at 1.0 A/g and a rate capability of 400 F/g at 50 A/g based on the three-electrode configuration.As an electrode for a symmetric capacitor,a specific capacitance of 299 F/g at 0.5 A/g was exhibited,and the specific capacitance retained 96%of the initial capacity at 5 A/g after 10,000 cycles.Furthermore,under the power density of 249.6 W/kg in 6 mol/L KOH,a high energy density of 10.34 Wh/kg was obtained.The excellent charge storage capability benefited from its interconnected hierarchical pore structure with high accessible surface area and the suitable amount of oxygen-containing functional groups.Thus,an effective strategy to synthesize HPC for high-performance supercapacitors serves as a promising way of converting coal into advanced carbon materials.