摘要
High-energy-density lithium metal batteries(LMBs)are widely accepted as promising next-generation energy storage systems.However,the safety features of practical LMBs are rarely explored quantitatively.Herein,the thermal runaway behaviors of a 3.26 Ah(343 Wh kg^(−1))Li|LiNi_(0.5)Co_(0.2)Mn_(0.3)O_(2)pouch cell in the whole life cycle are quantitatively investigated by extended volume-accelerating rate calorimetry and differential scanning calorimetry.By thermal failure analyses on pristine cell with fresh Li metal,activated cell with once plated dendrites,and 20-cycled cell with large quantities of dendrites and dead Li,dendrite-accelerated thermal runaway mechanisms including reaction sequence and heat release contribution are reached.Suppressing dendrite growth and reducing the reactivity between Li metal anode and electrolyte at high temperature are effective strategies to enhance the safety performance of LMBs.These findings can largely enhance the understanding on the thermal runaway behaviors of Li metal pouch cells in practical working conditions.
出处
《SusMat》
2022年第4期435-444,共10页
可持续发展材料（英文）
基金
Beijing Municipal Natural Science Foundation(Z200011)
National Key Research and Development Program(2021YFB2500300)
National Natural Science Foundation of China(22179070,22075029,U1932220),the“Shuimu Tsinghua Scholar Program of Tsinghua University”,and Mercedes-Benz AG.Xiang-Qun Xu and Xin-Bing Cheng contributed equally to this work.