摘要
Ni-rich layered oxides are considered promising cathodes for advanced lithium-ion batteries(LIBs)in the future,owing to their high capacity and low cost.However,the issues on structural and interfacial stability of Ni-rich cathodes still pose substantial obstacles in the practical application of advanced LIBs.Here,we employ a one-step method to synthesize a B-doped and La_(4)NiLiO_(8)-coated LiNi_(0.82)5Co_(0.115)Mn_(0.06)O_(2)(BL-1)cathode with reliable structure and interface,for the first time.The La_(4)NiLiO_(8)coating layer can prevent cathodes from electrolyte assault and facilitate Li+diffusion kinetics.Moreover,B-doping can effectively restrain the pernicious H_(2)-H_(3) phase transition and adjust the orientation of primary particles to a radial alignment,which is obstructive to the arise of microcracks induced by the change of anisotropic volume.Specifically,when tested in pouch cells,the BL-1 cathode exhibits outstanding capacity retention of 93.49%after 500 cycles at 1 C.This dual-modification strategy dramatically enhances the stability of the structure and interface for Ni-rich cathode materials,consequently accelerating the commercialization process of high-energy–density LIBs.
基金
financially supported by the National Natural Science Foundation of China(51774051,52072323,52122211)
the Science and Technology Planning Project of Hunan Province(2019RS2034)
the Hunan High-tech Industry Science and Technology Innovation Leading Plan(2020GK2072)
the Changsha City Fund for Distinguished and Innovative Young Scholars(KQ1707014)。